Corps broyants et médias de broyage destinés aux circuits de comminution : billes forgées, billes coulées et billes céramiques.
| Description | Spécification | Conditionnement |
|---|---|---|
| Forged Grinding Ball 40mm – 125mm ø Diameter | C: 0.6% – 1.00% | Si: 0.17% – 0.37% | Mn: 0.6% – 1.2% | P&S: ≤0.035% | Cr: 0.4% – 0.9% | 850kg drums 1,000kg bags 2,000kg bags |
| Low Chromium – Cast Grinding Ball – 40mm – 125mm ø Diameter | C: 2.1% – 3.60% | Si: ≤ 1.5% | Mn: ≤ 1.0% | P&S: ≤0.10% | Cr: 1%-2% | 850kg drums 1,000kg bags 2,000kg bags |
| High Chromium – Cast Grinding Ball – 40mm – 100mm ø Diameter | C: 2.0% – 3.30% | Si: ≤ 1.2% | Mn: ≤ 1.0% | P&S: ≤0.06% | Cr: 11% | 850kg drums 1,000kg bags 2,000kg bags |
| Ceramic Beads CB 502 – 2.0 to 7.0mm | ZrO₂ – 20% : SiO₂ – 35% : Al₂O₃ – 40% : Other 5% | Specific Density as gram /cm3 > 3.2 | Bulk Density as gram / cm³ – 2.05 – 2.25 | Moh’s Hardness – 8 | 25kg bags 1,000kg bags |
| Yttrium Stabilized Ceramic Beads CB 505 – 2.0 to 7.0mm | ZrO₂ – 94.6% : Y₂O₃ – 5.2 % : Other 0.2% |Specific Density as gram /cm3 > 6.0 | Bulk Density as gram / cm³ – > 3.7 | Moh’s Hardness – 9 | 25kg bags 1,000kg bags |
| ZTA W Ceramic Beads CB 522 2.0 to 7.0mm | ZrO₂ + Hfo₂ – 2% : SiO₂ – 4% : Al₂O₃ – 90% : Other 4% |Specific Density as gram /cm3 > 3.65 | Bulk Density as gram / cm³ – 2.3 | Moh’s Hardness – 9 | 25kg bags 1,000kg bags |
| Oversized Ceramic Beads 25-75mm – Available in ZTA W composition. | ZrO₂ + Hfo₂ – 2% : SiO₂ – 4% : Al₂O₃ – 90% : Other 4% | Specific Density as gram /cm3 > 3.65 | Bulk Density as gram / cm³ – 2.3 | Moh’s Hardness – 9 | 25kg bags 1,000kg bags |
Les conditionnements indiqués sont les formats standards. D’autres formats peuvent être étudiés selon vos volumes.